WEICON LOCK PEN SYSTEM AN 305-10 , 50 ml

high viscosity

high strength

hard to disassemble

Gasketing of flanges, gearboxes and other motor housings, high temperature resistant

Technical Data

Colour
orange

Viscosity at +25°C (+77°F) according to Brookfield
70.000 – 300.000 ht mPa·s

Max. gap bridging
0,5 mm

Breakaway strength (Thread)
18 – 25 Nm

Prevailing stregth
15 – 25 Nm

Shear strength Nmm² (DIN 54452)
5 – 10 N/mm²

Final strength (100%) after
6 – 12 h

Temperature resistance
-60 to +200 °C

*Strength values based on M 10 screws, 8.8 grade, thickness of nut 0,8.d Static shear strength based on cylindrical parts of abt. Ø 13 mm, tolerance (D-d) = 0,05 mm, l/d = 0,88

Surface pre-treatment In general, WEICONLOCK does not require special pretreatment as slightly oily surfaces (e.g. on as received parts) will be tolerated. However, best results will be achieved on cleaned, degreased parts (use WEICON Surface Cleaner). If required, the parts should be slightly roughened.